Our dry chlorinated thermal oxidation is recommended for use in MOS and other active device fabrication processes. Using dry chlorinated thermal oxide can help your device to perform to its highest potential by eliminating metal ions.

We recommend adding a forming gas (N2/H2) anneal after oxidation to passivate dangling bonds. Dangling bonds at the silicon interface can have an effect on the insulating properties of your oxide. Adding a forming gas anneal will insure that you are the receiving the maximum benefit of your dry chlorinated oxide.

We also offer the opportunity to customize our standard process to meet your needs. In many cases the temperature, ramp rates, and gas flows can be modified to achieve the result you are looking for.

Specifications

Thickness range: 100Å - 2000Å
Thickness tolerance: 100Å+/-15Å, >200Å+/-5%
Within wafer uniformity: +/-3% or better
Wafer to wafer uniformity: +/-5% or better
Sides processed: Both
Refractive index: 1.456
Film stress: -320MPa (Compressive)
Wafer size: 50mm, 100mm, 125mm, 150mm, 200mm
Wafer thickness: 100µm - 2,000µm
Wafer material: Silicon, Silicon on Insulator
Temperature: 950C° - 1050C°
Gases: Oxygen
Chemical vapor: TransLC (Chlorine Source)
Equipment: Horizontal Furnace


MEMS Companies Semiconductor Devices Physical Vapor Deposition Thin Film Deposition Silicon Wafer Processing MEMS Sensors	Silicon Wafer Supplier Silicon Wafers \| SOI Wafers Silicon Wafer Processing Silicon Wafer Manufacturing Solar Wafers \| Quartz Wafers MEMS Mirror	PECVD Processing LPCVD Processing Wet Thermal Oxidation Thermal Annealing Sputtered Metals MEMS Manufacturer	SemiConductor Company Micro fabrication MEMS Manufacturer MEMS Foundry Thin Film Sputtering Site Map